Product Details:
|
| Product Name: | Wire Reinforced Glass Fabric | Material: | Fiberglass Fabric, Satinless Steel Wire |
|---|---|---|---|
| Yarn Type: | E-glass | Weight: | 600g/m2 |
| Thickness: | 0.6mm | Keywords: | Wire Inserts |
| Application: | Fire Doors And Fire Curtains | Good Features: | Water, Chemical, And Oil Resistant, Fire Resistant Insulation |
| High Light: | fiberglass fabric roll,woven fiberglass cloth |
||
Satinless Wire Reinforced 0.6mm Thickness Glass Cloth On Thermal Insulation Cover
1. Product Description:
Fiberglass cloth with ss wire inserts - a woven plain fiberglass fabric with inserted stainless steel (316) wire for added tensile strength. The stainless steel wires we use are stronger and more durable. Compared with other manufacturer that used 304 stainless wire, we provide much higher quality of stainless wire insert fiberglass cloth.
We twist multiple stainless steel wires with each expanded glass fiber yarn. You can choose only warp yarn insert stainless steel or choose both warp and weft yarn insert stainless steel.
The glass fiber fabric of Jiangnan insert thread is woven from high-quality glass fiber yarn and stainless steel wire, which has higher tensile strength, puncture resistance and heat resistance. Stainless steel wire can radiate heat on the entire fabric surface, thereby improving heat resistance and heat resistance time.
2. Table 1: 666 Product Description
| 666 Stainless Wire Fiberglass Fabric | |
| Weave | 8H Satin |
| Thickness | 0.6+/-0.05mm |
| Width | 100/120/155cm or customized |
| Length | 50/100m or customized |
| Weight | 6500g/m2 |
| Yarn Type | E-glass yarn+Satinless Wire |
| Warp and Weft Density | 39*38/In |
| Warp and Weft Tensile Strength | 2237*2316 (N/2.5cm) |
| Color | White |
| Package | Carton Box or Woven Bag |
3. Table 2:Safety Data Sheet
E-glass fiberglass yarn is a kind of glass with a very low alkaline content. Its composition that is Oxides is within the following percentages, our products are harmless to human body.
| SiO2 | 50.8-54% |
| Alkaline Oxides (Na2O,K2O) | <1% |
| CaO | 21-24% |
| MgO | <2% |
| B2O3 | 6-10% |
| AhO3 | 13-15% |
| TiO2 | <0.8% |
| Fe2O3 | <0.5% |
| F2 | <1% |
4. Product Features:
Temperature Resitance up to 600 degrees
Higher warp and weft density
Larger weight per unit area and higher strength
Good hand feeling, much softer compared with other manufacturer
Fire resistance and heat resistance
High performance in chemical
5. Application:
Fire curtain, welding curtain
Fabric expansion joint
Lagging, gaskets and seals
Removable insulation pad and jacket
Welding blanket and equipment protection
Fire and heat insulation
6. More Detail Images
| 1000F/550℃: Stainless Steel Reinforced Fiberglass Fabric | |||||
| No | Type | Width (mm) | Weight(g/m2) | Thickness (mm) | Weave |
| 1 | 666 ss | 100/120/155 | 600 | 0.6 | Satin |
| 2 | Plain Weave SS | 100/120/155 | 1100 | 1.0 | Plain |
| 3 | 2025 ss | 100 120 155 | 600 | 0.75 | 1/3 Twill |
| 4 | M30 ss | 100/120/155 | 1200 | 1.2 | Plain |
Contact Person: Mr. Angelo Cheng
Tel: 86 13776220396
Fax: 86-512-52565400