Product Details:
|
| Product Name: | Non-Alkali 3786 Fiberglass Fabric | Thickness: | 1.3mm |
|---|---|---|---|
| Weight: | 1300gsm | Material: | A High-performance With High Temperature Fabric |
| Technique: | Produced Of Filament Fiberglass Yarns | Usage: | Used In Almost All Industries For Heat Protection |
| Application: | Heat Shields, Welding Curtains | Surface Treatment: | Available With Acrylic, Aluminum, Silicone, Pu And So On. |
| High Light: | plain weave fiberglass cloth,woven fiberglass cloth |
||
High Strength 3786 Fiberglass Fabric Cloth Thickness 1.0mm For Removable Pads
1. Product Description:
The Fiberglass cloth is produced by Suzhou Changshu Jiangnan Co, weaving by warp and weft yam according to certain rule. 3786 Glass Fiber Fabric is an excellent performance inorganic nonmetallic material, the main material for this product is fiberglass. It has good corrosive, acid and alkall resistance. It is a kind of idea high temperature resistance material due to it has satisfactory heat resistance and high mechanical strength. Fiberglass fabric is a light weight material which has moderate tensile and compressive strength. This cloth has been used in many industrial fields. Satin glass fiber fabric has excellent high-temperature protective properties, and surface appearance. the design of high strength glass cloth for yacht.
2. Table 1: 3786 Product Description
| 3786 | ||
| Item Model | 3786 Fiberglass Fabric | |
| Description | Woven Fiberglass Cloth | |
| Weave Structure | 12H Satin Weave | |
| Weight | 1300gsm | |
| Thickness | 1.2mm | |
| Yarn Type | Warp | EC9 136 1*2 |
| Weft | EC9 136 1*2 | |
| Thread Count | Warp | 16±1 ends/cm |
| Weft | 13±1 picks/cm | |
| Break Strength | Warp | 10000 N/5cm |
| Weft | 5000 N/5cm | |
| LOI | < 0.4% | |
| Working Temperature | ≤550℃ | |
3. Table 2:Safety Data Sheet
E-glass fiberglass yarn is a kind of glass with a very low alkaline content. Its composition that is Oxides is within the following percentages, our products are harmless to human body.
| SiO2 | 50.8-54% |
| Alkaline Oxides (Na2O,K2O) | <1% |
| CaO | 21-24% |
| MgO | <2% |
| B2O3 | 6-10% |
| AhO3 | 13-15% |
| TiO2 | <0.8% |
| Fe2O3 | <0.5% |
| F2 | <1% |
4. Product Features:
This kind of material that is fiberglass has good corrosive, acid and alkali resistance. Product 3786 made from this material is an ideal high temperature resistance material due to it has satisfactory heat resistance and high mechanical strength.
5. Application:
1. Thermal Insulation and Heat Protection
2. Removable Pads and Welding Blanket
3. Expansion Joint and Piping
4. Basic Material for Coating, Impregnating and Laminating
| No | Type | Width (mm) | Weight(g/m2) | Thickness (mm) | Weave |
| 1 | 7781 | 107 127 157 207 254 | 300±8 | 0.22 | 8HS |
| 2 | 7581 | 107 127 157 207 254 | 300±8 | 0.23 | 8HS |
| 3 | 3732 | 107 127 157 207 254 | 425±8 | 0.4 | 1/3 Twill |
| 4 | 332 | 107 127 157 207 254 | 427±8 | 0.36 | 4HS |
| 5 | 666 | 107 127 157 207 254 | 640±20 | 0.6 | 8HS |
| 6 | 3784 | 107 127 157 207 254 | 870±20 | 0.8 | 8HS |
| 7 | 3786 | 107 127 157 207 254 | 1450±20 | 1.2 | 12HS |
| 8 | 3788 | 107 127 157 207 254 | 1650±20 | 1.6 | 12HS |