Product Details:
|
| Product Name: | Stainless Steel Wire Fiberglass Fabric | Material: | 100% Fiberglass+Steel Wire |
|---|---|---|---|
| Weight: | 710g/sqm (20.88 Oz./Sq.Yd.) | Coating: | Both Side Polyurethane Coating |
| Technology: | Stainless Steel Wire | Application: | Smoke And Fire Curtain |
| Standing Temperature: | From -100℃ To 650℃ | Good Features: | Corrosion Resistance/Acid Resistance /Moisture Resistance |
| High Light: | SS Wire Inserts Fiberglass Cloth,Smoke Fire Curtain Pu Coated Fabric,Moisture Resistance Pu Coated Fabric |
||
Fiberglass Cloth With SS Wire Inserts Pu Coated Fabric Used For Smoke And Fire Curatin
1. Description:
Fiberglass Cloth with SS Wire Inserts is a woven glass medium-weight satin fabric with inserted stainless steel (T316) wire for added tensile strength and coated with fire retardant aluminum pigmented polyurethane on both sides of the fabric.. Applications for this fabric include use as a hot-side insulation fabric, flange and valve covers, weld curtains, and stress relief blankets. The material is resistant to chemicals and offers good heat and flame protection in service applications up to 1,000°F.
Specification: 666 Stainless Wire Fiberglass Fabric
Nominal Width 40”
Nominal Weight 21 oz
Nominal Thickness: 0.024In
Base Cloth Temperature Resistance 1000°F
Content: Warp: 100% Fiberglass Yarns
Fill: Stainless Steel Wire (T316) Plied With Fiberglass Yarns
Weave can be one-directional (stainless is only inserted in warp yarn) or two-directional (stainless is inserted in both warp yarn and weft yarn)
Count Warp: 15
Fill: 14.5
2. Table 1: TDS for 666 polyurethane coated polyester fabric with Stainless Wire
| 666 Stainless Wire Fiberglass Fabric with Double-sided Pu Coating | |||
| Item Model | 666 Steel Wire Fiberglass Fabric | ||
| Description | Tension Strengthen Fiberglass Cloth | ||
| Weave Structure | Satin Weave | ||
| Weight | 650±60gsm | ||
| Thickness | 0.6mm | 0.039 inch | |
| Yarn Type | Warp | EC9 68 1*3 | G75/3 + Stainless Wire |
| Weft | EC9 68 1*3 | G75/3 + Stainless Wire | |
| Thread Count | Warp | 15±1 ends/cm | 38±3 Per Inch |
| Weft | 14.4±1 picks/cm | 36±3 Per Inch | |
| Break Strength | Warp | 2237 N/5cm | 447 lbs/inch |
| Weft | 2316 N/5cm | 463.2 lbs/in | |
| PU Coating Weight | 50±10gsm | ||
| Color | Silver, Dark Grey | ||
| LOI | < 5% | ||
| Working Temperature | ≤550℃ | ||
3. Properties:
Halogen-free, asbestos-free, non-itchy.
Chemical resistance, waterproof, weatherproof, abrasion resistance.
Thick but soft material, easy to be cut and sewn
Higher tensile strength.
316 stainless steel provides durable and good abrasion resistance.
Withstand high temperatures up to 700℃.
4. Application:
Thermal insulation jacket, mattress, and pad
Expansion joints and compensators
5. Much More Choice for PU coating:
This kind of raw material is normally used on welding & fire protection, thermal insulation jackets, mattress, expansion joint belt, a protective scrim of insulation wool, composite reinforcement
| Type | Thickness | Weight | ||
| mm | inch | g/m2 | oz/yd2 | |
| 3732 with Double-sided Pu Coating | 0.5 | 0.0197 | 460±20 | 13.6 |
| 3732 with Double-sided Silicone Coating | 0.5 | 0.0197 | 540±20 | 15.9 |
| 3734 with Double-sided Pu Coating | 0.5+ | 0.02 | 510±20 | 15.04 |
| 3734 with Double-sided Silicone Coating | 0.5+ | 0.02 | 590±20 | 17.4 |
| Stainless Steel Wire Insert Fiberglass cloth with Double-sided Pu Coating | 0.6 | 0.0236 | 700±20 | 21 |
| 800 with Double-sided Pu Coating | 0.8 | 0.0315 | 820±30 | 24.18 |
| 800 with Double-sided Silicone Coating | 0.8 | 0.0315 | 1050±30 | 32.05 |
| Other thicknesses can be customized according to your Requirements | ||||
6. Detail Images for PU Coated Fiberglass Cloth
7. Applications
8: Packing
Standard length: 50meters or 100 meters
One carton one roll
20 cartons per pallet