Product Details:
|
| Product Name: | Ceramic Fiber Bulk | Application: | Heat Insulation |
|---|---|---|---|
| Thikcness: | 0.5-10mm | Width: | 610,1200mm |
| Grade: | HIgh Grade | Long Time Working Temperature: | 1260℃ |
| Density: | 210kg/m3 | Color: | Pure White |
| Chemical Composite: | Al2O3 47% | ||
| High Light: | vermiculite coated fiberglass cloth,flame retardant fabric |
||
Refractory Ceramic Fiber Cotton 1400C Fireproof Thermal Insulation
Ceramic paper is made from high-purity ceramic fiber by adding a small amount of binder which will completed burnt out during using process, through production technology with scientific selection and strict control binding. The product shows excellent thermal insulation properties and construction performance, suitable for use in deep processing (multi-layer composite, punching, etc.); and excellent resistance to molten infiltration, allowing itself to be used for casting washer separation in the construction and glass industries.
Characteristics:
1. Low thermal capacity
2. Low thermal conductivity
3. Excellent electrical insulation properties
4. Excellent machining performance
5. High strength, tear resistance
6. High flexibility
7. Low shot content
Application:
1. Insulation material for instruments and heating element
2. Insulation material for automobile and aerospace industry
3. Expansion joints filling material
4. Isolation for construction material, metallurgy and glass industries,
5. Molten metal sealing gasket
6. Fireproof material
7. Substitute for glass fiber and asbestos fiber
| Name | Type | Thickness Range |
| Ceramic Paper |
TXZ-1350 |
1-5mm |
|
0.4-1mm, 5-8mm |
||
|
TXZ-1260 |
1-5mm | |
|
0.4-1mm, 5-8mm |
||
|
TXZ-1400 |
1-5mm | |
|
0.4-1mm, 5-8mm |
TDS
| Name | TXZ-1260 | TXZ-1350 | TXZ-1400 | |
| Weight | 180±20 | 180±20 | 180±20 | |
| Theoretical Temperature Resistance | 1260oC | 1350oC | 1400oC | |
| Long-time Use T | 1000-1100oC | 1100-1200oC | 1200-1250oC | |
| Weight Loss | <=8% | <=8% | <=8% | |
| Al2O3 | >=42 | >=52 | >=49 [Zero>=3] | |
|
Linear Shrinkage (1000oC-24h) |
<=4% | <=4% | <=4% | |
| Al2O3+SiO2 | >=94 | >=94 | ||
|
Thermal conductivity [W/m k]
|
400oC | <=0.1 | <=0.1 | <=0.1 |
| 800oC | <=0.12 | <=0.12 | <=0.12 | |
| 1000oC | <=0.135 | <=0.135 | <=0.135 | |
| Type | Meaning |
| TXZ-1260 |
Moderate soft and hard Good strength Bent Widely application |
| TXZ-1260R |
High Strength Easy Bend |
| TXZ-1260R+ |
Good Softness Used for Warpping No rebound |
| TXZ-1260Y |
High strength Not easy to crack Used for pad |
| TXZ-1260Y+ |
Highest strength No layers Used for punching |